PrimaCreator Value Flex UV Resin – 500 ml – Black

54,90 με ΦΠΑ

When you want astonishing results for less cost than many other brands – PrimaCreator VALUE resin should be your first choice!

Out of stock

Προσθήκη στα Αγαπημένα
Προσθήκη στα Αγαπημένα


When you want astonishing results for less cost than many other brands – PrimaCreator VALUE resin should be your first choice!

Resin from our VALUE line is a high-quality resin made from the best materials.
Your prints cures in sunlight or a UV curing chamber. When the curing is finished, the result is a flexible print with very small shrinkage and very soft to the touch.

The finished print is a solid color part with a beautiful matte surface with excellent details and smooth layer transitions.
Flexible resin is the perfect resin when you are looking for high detail results that needs to have a very high impact strength. The shore hardness of 65-75 D together with an incredible elongation at break of 130% makes it a resin that can use in many applications and areas.

VALUE resin is developed to perform well on low powered DLP machines such as the Wanhao Duplicator 7, SparkMaker Anycubic Photon, Zortrax Inkspire and other printers that uses UV light for curing.

Optimized for UV Lightsource 395 – 405 nm.

Fast curing time, 4 – 12 (depending on color) seconds per layer for quicker prints.
After printing, clean you print in IPA (Isopropyl Alcohol) to rinse of extra resin left on the model.

When it´s time for curing you can use sunlight or a uv curing chamber.
Depending on print the curing times can vary:

In a UV light curing chamber, it will take about 2-5 minutes.
In sunlight, 10-20 minutes.
In daylight on a cloudy day it can take up to 60 minutes.

Additional information

Weight 0,7 kg



500 ml

Flexural modulus 1.882 – 2.385 MPa
Flexural strength 40-70 MPa
Hot deformation temp. 80 ℃
Thermal expansion 95*E-6
Volume shrinkage 3.72 – 4.24%
Linear shrinkage 1.05 – 1.35%
Tensile strength 30 – 52 MPa
Tensile modulus 1.779 – 2.385 MPa
Elongation at break 130%
Hardness (Shore D) 65 – 75D
Glass transition temp. 100 ℃
Density 1.05-1.25g/cm3
Notched impact strength 41-48 j/m
Viscosity 150-300 MPa·s
Curing time 4 – 12s for layer thickness 0.05 mm
Bottom layer 40 – 60 s