PrimaCreator Value Water Washable UV Resin – 1000 ml – Chromatic Silver
€64,90 με ΦΠΑ
When you want astonishing results for less cost than many other brands – PrimaCreator VALUE resin should be your first choice!
The new water washable resin from PrimaCreator is the latest addition in the range and offers the same quality as our other resins.
In contrast to most other resin the water washable resin from PrimaCreator doesn’t require any chemicals for removing uncured material from the print. You just simply rinse it in regular tap water, and it comes out clean and ready to be cured.
This, of course, is the best choice for both you and the environment.
Resin from our VALUE line is a high-quality resin made from the best materials.
Your prints cures in sunlight or a UV curing chamber. When the curing is finished, the result is a rock-hard print with very small shrinkage.
The finished print is a solid color part with a beautiful semi matte surface with excellent details and smooth layer transitions.
If you go for the transparent resin you will have a crystal-clear transparency which is truly stunning.
VALUE resin has many benefits over other brands of comparable resins.
The most noticeable is that it doesn’t smell very much.
VALUE resin is developed to perform well on low powered DLP machines such as the Wanhao Duplicator 7, SparkMaker Anycubic Photon, Zortrax Inkspire and other printers that uses UV light for curing.
Optimized for UV Lightsource 395 – 405 nm.
Fast curing time, 4 – 8 seconds per layer for quicker prints.
After printing clean you print in regular water or PrimaCreator Resin Cleaner.
When it´s time for curing you can use sunlight or a UV curing chamber.
Depending on print the curing times can vary:
In a UV light curing chamber, it will take about 2-5 minutes.
In sunlight, 10-20 minutes.
In daylight on a cloudy day it can take up to 60 minutes.
1000 ml ( 1 liter )
|Flexural modulus：1.882-2.385Mpa:||Elongation at break：4-10%|
|Flexural strength ：40-58MPa||Hardness(Shore D)：85-88 D|
|Hot deformation temp.：80℃||Glass transition temp.：100℃|
|Thermal expansion：95*E-6||Density：1.05—1.25 g/cm3|
|Volume shrinkage：3.35%-4.24%||Notched impact strength:41-48j/m|
|Tensile modulus：1.779—2.385 MPa|