PrimaSelect PLA Chameleon – 1.75mm – 750 g – Silver / Gold
€44,90 με ΦΠΑ
Chameleon is a new filament from PrimaCreator with a unique look. The filament is made up from two strands of filament which results in a print that has dual colors. The effect is stunning as the print seems to “change color” as you turn it and the light reflects in different ways.
- Made from virgin PLA
- Changes color when you turn it or depending on light
- Comes in a variety of different color schemes
- Prints like regular PLA
- No hazardous fumes or unpleasant smell
- Low risk of warping
Out of stock
Chamelon is a new filament from PrimaCreator with a unique look to it. The filament is made up from two strands of filament which results in a print that has dual colors. The effect is stunning as the print seems to “change color” as you turn it and the light reflects in different ways.
PLA is one of the most common used 3d-print materials in the world, it´s non-toxic and has a no unpleasant smell when you print with it. Because of its thermal characteristics it’s easy to get great prints. Filament from Prima Creator comes on a transparent spool which makes it easy to see how much filament there are left on the spool. Polylactic acid (PLA) is a bio-degradable polymer that is produced from lactic acid, which can be fermented from crops such as corn.
PrimaSELECT PLA CHAMELEON adheres to BuildTak, PEI or glass plates which are coated with adhesive spray or PrimaFIX. A heated build platform is not essential. However, if your 3D printer has one, we recommend a setting of 35 – 60 °C for best 3D printing results. Recommended print temperature is 205 – 225°C
|Recomended Printing Temp Min||205 ºC|
|Recomended Printing Temp Max||225 ºC|
|Recomended Printbed Temperature Min||35 ºC|
|Recomended Printbed Temperature Max||60 ºC|
|Specific gravity||1,24 g/cm3 ISO 1183|
|Vicat softening temp||58,2 °C ISO 306/B50|
|Tensile strength||71 MPa ISO 527|
|Elongation at yield||3,2 % ISO 527|
|Elongation at break||3,6 % ISO 527|
|Impact Strength||2,6 KJ/m2 ISO 1791eA|